Prof. Dr. Wolfgang Knoll

Wolfgang Knoll1,2, Klaus Müllen1, Kaoru Tamada3 and Ming-Yong Han2
1 Max-Planck-Institute for Polymer Research, Mainz, Germany
2 Department of Materials Science, National University of Singapore, Singapore
3 National Institute of Advanced Industrial Science and Technology (AIST), Tsukuba, Japan

Nanoscopic Building Blocks from Polymers, Metals and Semiconductors for Hybrid Architectures

This contribution summarizes some of our efforts in synthesizing building blocks of organic/polymeric materials, as Au colloids or as semiconducting quantum dots, for the construction of nanoscopic hybrid aggregates and architectures.

Firstly, polyphenylene dendrimers are introduced as shape-persistent organic building blocks with a strictly monodisperse particle size distribution within the nanometer range. The possibility for the introduction of different functionalities in the core, the scaffold or the periphery of the dendrimers offers their use as interesting modules for photonic, electronic or bioactive structures and supramolecular functional assemblies. Thus dendrimers complement the available set of nanoscopic building blocks made from metals and semiconductors.

The next example concerns metallic nanostructures. Firstly, we focus on gold nanoparticles capped by unsymmetrical azobenzene disulfides that were synthesized in order to investigate the efficiency of photoisomerization on a colloidal gold surface. The average size of the particles was determined to be ~5.2 ± 1.3 nm from transmission electron microscope (TEM) images. The photoisomerization reaction of the azobenzene-capped gold nanoparticles was studied by UV-vis absorption spectroscopy in toluene. The reaction kinetics were identical to that of the free molecules with no deviations from a first-order plot for both trans-to-cis and cis-to-trans photoisomerization, suggesting no steric hindrance throughout the whole reaction process.

The last example concerns semiconducting nanoparticles, quantum dots (QDs), as another class of nanoscopic building blocks with interesting properties. We synthesized high-quality ZnxCd(1-x)Se nanocrystals at high temperatures by incorporating stoichiometric amounts of Zn and Se into pre-prepared CdSe nanocrystals. With increasing Zn content, a composition-tunable emission across most of the visible spectrum could be demonstrated by a systematic blue-shift in emission wavelength. The photoluminescence (PL) properties for the obtained ZnxCd1-xSe nanocrystals (PL efficiency of 70-85%, fwhm = 22-30 nm) are comparable to those for the best reported CdSe-based QDs. In particular, they also have good PL properties in the blue spectral range. Moreover, the alloy nanocrystals can retain their high luminescence (PL efficiency of over 40 %) when dispersed in aqueous solutions and maintain a symmetric peak shape and spectral position under rigorous experimental conditions.

J. H. Hernandez-Lopez et al., Functional Polymers as Nanoscopic Building Blocks, Mat.Sci & Eng. 23 (2003) 267-274.
A. Manna et al., Optimized Photoisomerization on Gold Nanoparticles Capped by Unsymmetrical Azobenzene Disulfides, Chem.Mat 15 (2003) 20-28
X. H. Zhong et al., Composition-Tunable ZnxCd(1-x)Se Nanocrystals with High Luminescence and Stability, J.Am.Chem.Soc. 125 (2003) 8589-8594.

15. Mitglieder laden Mitglieder ein
ZOOM-Meeting | 13. Nov. 2021

Treffen der Regionalgruppe

ZOOM-Meeting | 17. Nov. 2021

Neues vom Club 02/2021

JSPS-Club bei der Nippon Connection
Die Deutsche Gesellschaft der JSPS-Stipendiaten e.V. (JSPS-Club) und das JSPS Bonn Office stellen sich beim Nippon Connection Filmfestival vor.


„Orden der Aufgehenden Sonne am Halsband, goldene Strahlen“ (旭日中綬章) der japanischen Regierung für Club-Mitglieder Prof. Dr. Werner Pascha und Prof. Dr. Peter Hennicke